Grain boundary wetting in the Al-Mg system and synthesis of magnesium diboride in contact with melt

Abstract

The interaction between a Mg-containing melt and B under conditions of partial and complete wetting of Al/Al grain boundaries by Al-Mg melt has been investigated. The study was performed on Al polycrystals with Mg contents of 5, 10, 15, 18, and 25 wt %. Correspondingly, the Mg content in the melt was determined by the liquidus line and was in the range from 5 to 30 wt %. The obtained metal-matrix composites were investigated by light and scanning electron microscopy, electron-probe microanalysis, and X-ray diffraction. The possibility of synthesizing MgB2 in the contact with a melt having a relatively low Mg content (from 15 to 30 wt %) has been demonstrated.